EN10216-2 TC2 P235GH 1.0345 Seamless Alloy Steel Tubes for Caldera, Boiler
YuHong Group, one of the leading suppliers in China,we supply alloy seamless steel boiler tubes with high quality to our customers and have many experiences in exporting. P235GH EN 10216-2 Tubes which manufacture from carbon as well as low alloy steel grades tend to be resistant to loads under very high pressure and high temperatures.
Charastertistic: Resistance, Pressure Resistance, Good Weldability, Corrosion Resisitance, Versatility
The EN 10216-2 standard specifies the requirements for seamless non-alloy and alloy steel tubes for specified elevated temperature conditions. Primarily used in the construction of pressure equipment such as boilers, heat exchangers, and pipelines.
Chemical Composition % Max
| C | Si | Mn | P | S | Cr | Mo | Ni | Al a | Cu b | Nb c | Ti c | V c | Cr+Cu+Mo+Ni |
| 0.16 | 0.35 | 1.2 | 0.025 | 0.02 | 0.3 | 0.08 | 0.3 | 0.02 | 0.3 | 0.01 | 0.04 | 0.02 | 0.7 |
a This requirement is not applicable provided the steel contains a sufficient amount of other nitrogen binding elements which shall be reported.When using titanium, the producer shall verify that(Al+Ti/2)≥0,020%.
b Option 2: In order to fecilitae subsequent forming operations, an agreed maximum copper content lower than indicated and an agreed specified maximum tin content shall apply.
c The content of these elements need not to be reported unless intentionally added to the cast.
Mechanical Property
| Steel grades | Upper yield limit or yield strength ReH or Rp0,2 for wall thickness of t min | Tensile strength Rm |
Elongation A min% |
| T≤16 | 16＜T≤ 40 | 40＜T≤ 60 | 60＜T≤ 100 |
| MPa | MPa | MPa | MPa | MPa | I | t |
| P235GH | 235 | 225 | 215 | - | 360- 500 | 25 | 23 |
Applications
Pipeline
Oil Industries
Gas Distribution
Power Industries
Nuclear Power Generation
Heat Exchangers/Boilers/Condensers,etc
Welcome your inquiry of alloy steel boiler tubes to YUHONG Group!